Grade/Product Name: P-SIF-30

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 3.0 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1550 MPa ASTM D790
Tensile Strength at Yield 35 MPa ASTM D 638
Tensile Elongation at Yield 12 % ASTM D 638
Izod cImpactStrength(notched)at23° c 55 J/m ASTM D256
Vicat softening point (10 N) 156 °c ASTM D 1525
H.D.T (0.46 MPa) 94 °c ASTM D 648

Main Application: Extrusion (film yarn, monofilament, sheet)
Product Type: Homo polymer

1-1
1-3
1-2

Grade/Product Name: P-F-040

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 4.0 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1500 MPa ASTM D790
Tensile Strength at Yield 34 MPa ASTM D 638
Tensile Elongation at Yield 12 % ASTM D 638
Izod cImpactStrength(notched)at23° c 55 J/m ASTM D256
Vicat softening point (10 N) 156 °c ASTM D 1525
H.D.T (0.46 MPa) 94 °c ASTM D 648

Main Application: Extrusion of sheet for Thermoforming, Film Yarn &Monofilament
Product Type: Homo polymer

2-3
2-1
2-2

Grade/Product Name: P-SF-060

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 6.0 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1500 MPa ASTM D790
Tensile Strength at Yield 35 MPa ASTM D 638
Tensile Elongation at Yield 12 % ASTM D 638
Izod cImpactStrength(notched)at23° c 30 J/m ASTM D256
Vicat softening point (10 N) 154 °c ASTM D 1525
H.D.T (0.46 MPa) 94 °c ASTM D 648

Main Application: Extrusion (film yarn, monofilament, sheet)
Product Type: Homo polymer

3-3
3-2
3-4
3-1

Grade/Product Name: P-SI-080

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 8.0 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1550 MPa ASTM D790
Tensile Strength at Yield 36 MPa ASTM D 638
Tensile Elongation at Yield 12 % ASTM D 638
Izod cImpactStrength(notched)at23° c 36 J/m ASTM D256
Vicat softening point (10 N) 154 °c ASTM D 1525
H.D.T (0.46 MPa) 93 °c ASTM D 648

Main Application: Injection molding
Product Type: Homo polymer

4-1
4-2
4-3

Grade/Product Name: P-FI-090

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 10 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1550 MPa ASTM D790
Tensile Strength at Yield 35 MPa ASTM D 638
Tensile Elongation at Yield 12 % ASTM D 638
Izod cImpactStrength(notched)at23° c 37 J/m ASTM D256
Vicat softening point (10 N) 154 °c ASTM D 1525
H.D.T (0.46 MPa) 95 °c ASTM D 648

Main Application: Injection molding
Product Type: Homo polymer

5-1
5-2
5-3

Grade/Product Name: P-I-110

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 12 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1400 MPa ASTM D790
Tensile Strength at Yield 34 MPa ASTM D 638
Tensile Elongation at Yield 12 % ASTM D 638
Izod cImpactStrength(notched)at23° c 35 J/m ASTM D256
Vicat softening point (10 N) 154 °c ASTM D 1525
H.D.T (0.46 MPa) 95 °c ASTM D 648

Main Application: Injection molding
Product Type: Homo polymer

6-3
6-1
6-2

Grade/Product Name: P-FI-160

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 16 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1550 MPa ASTM D790
Tensile Strength at Yield 33 MPa ASTM D 638
Tensile Elongation at Yield 12 % ASTM D 638
Izod cImpactStrength(notched)at23° c 30 J/m ASTM D256
Vicat softening point (10 N) 154 °c ASTM D 1525
H.D.T (0.46 MPa) 95 °c ASTM D 648

Main Application: Fiber extrusion
Product Type: Homo polymer

7-1
7-3
7-2

Grade/Product Name: P-YI-180

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 18 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1550 MPa ASTM D790
Tensile Strength at Yield 33 MPa ASTM D 638
Tensile Elongation at Yield 12 % ASTM D 638
Izod cImpactStrength(notched)at23° c 30 J/m ASTM D256
Vicat softening point (10 N) 154 °c ASTM D 1525
H.D.T (0.46 MPa) 95 °c ASTM D 648

Main Application: Fiber extrusion (CF, Staple)
Product Type: Homo polymer

8-4
8-2
8-3

Grade/Product Name: P-YI-220

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 22 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1650 MPa ASTM D790
Tensile Strength at Yield 35 MPa ASTM D 638
Tensile Elongation at Yield 12 % ASTM D 638
Izod cImpactStrength(notched)at23° c 30 J/m ASTM D256
Vicat softening point (10 N) 154 °c ASTM D 1525
H.D.T (0.46 MPa) 95 °c ASTM D 648

Main Application: Fiber extrusion (CF, Staple)
Product Type: Homo polymer

9-1
9-3
9-4
9-2

Grade/Product Name: P-YI-250

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 25 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1500 MPa ASTM D790
Tensile Strength at Yield 34 MPa ASTM D 638
Tensile Elongation at Yield 12 % ASTM D 638
Izod cImpactStrength(notched)at23° c 30 J/m ASTM D256
Vicat softening point (10 N) 154 °c ASTM D 1525
H.D.T (0.46 MPa) 95 °c ASTM D 648

Main Application: Fiber extrusion (CF, Staple)
Product Type: Homo polymer

10-2
10-3
10-1

Grade/Product Name: P-YI-300

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 30 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1500 MPa ASTM D790
Tensile Strength at Yield 32 MPa ASTM D 638
Tensile Elongation at Yield 13 % ASTM D 638
Izod cImpactStrength(notched)at23° c 30 J/m ASTM D256
Vicat softening point (10 N) 152 °c ASTM D 1525
H.D.T (0.46 MPa) 94 °c ASTM D 648

Main Application: Injection Molding- Extrusion (BCF-CF)
Product Type: Homo polymer

11-1
11-5
11-4
11-3
11-6
11-2

Grade/Product Name: P-YI-350

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 35 dg/min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1450 MPa ASTM D790
Tensile Strength at Yield 32 MPa ASTM D 638
Tensile Elongation at Yield 10 % ASTM D 638
Izod cImpactStrength(notched)at23° c 30 J/m ASTM D256
Vicat softening point (10 N) 152 °c ASTM D 1525
H.D.T (0.46 MPa) 90 °c ASTM D 648

Main Application: Extrusion (BCF, CF)
Product Type: Homo polymer

12-2
12-1
12-5
12-4
12-6
12-3

Grade/Product Name: P-CR-380

Test/Composition value unit Method
Melt flow rate(230° c/2.16 kg) 35-40 g/10min ASTM D 1238
Density 0.9 g/cm3 ASTM D 1505
Flexural Modulus 1500 MPa ASTM D790
Tensile Strength at Yield 33 MPa ASTM D 638
Tensile Elongation at Yield 8 % ASTM D 638
Izod cImpactStrength(notched)at23° c 30 J/m ASTM D256
Vicat softening point (10 N) 155 °c ASTM D 1525
H.D.T (0.46 MPa) 91 °c ASTM D 648